Development of a High Abrasion Resistance Shoe Sole Incorporating Four Different Silica Grades
No Thumbnail Available
Date
2021
Journal Title
Journal ISSN
Volume Title
Publisher
Uva Wellassa University of Sri Lanka
Abstract
Silica used as active reinforcing filler to improve high abrasion resistance in Rubber. In this study,
the effect of four different silica grades (silica MP BET 161-190, silica powder newsil micro peral,
silica 355GR and silica BET higher grade) on the abrasion resistance and other properties of the shoe
sole have been studied. In this study type of silica grades was changed while keeping all the other
ingredients and their amounts constant. The abrasion resistance was determined using DIN 53516 test
method and the hardness, specific gravity, tensile strength and elongation at break were determined
by following the respective ISO and ASTM standards. The results of the study showed that all four
silica grades incorporated shoe soles have achieved acceptable abrasion resistance values. Achieved
abrasion resistance value for shoe sole is maximum 350mm3. However, silica MP BET 161-190 has
289 mm3 which is also a quite higher abrasion resistance with a minimum loss of rubber in abrasion
compared to other three silica grades. When considering the effect of silica grade on the physical
properties of rubber compound, both silica MP BET 161-190 and 355GR grades showed acceptable
values for all tested hardness, specific gravity, tensile strength and elongation at break of silica MP
BET 161-190 grade incorporate sample were 48 IRHD, 1.088,17 MPa and 676% respectively. While
silica 355GR incorporated sample were 51 IRHD, 17.1MPa and 631% respectively. However, both
silica powder newsil micro peral and silica BET higher grade incorporated samples showed poor
performance for the tested physical properties. Therefore, it can be concluded that, silica MP BET
161-190 is better performing as an active reinforcing filler with the highest abrasion resistance and a
minimum loss of rubber in abrasion compared to other three silica grades.
Keywords: Abrasion resistance; Physical properties; Shoe sole; Silica grades
Description
Keywords
Mineral Sciences, Materials Sciences, Export Agriculture, Shoe sole