Reducing Photocatalytic Degradation of Exterior Paint Prepared with TiO2

Simple item page
dc.contributor.authorDissanayake, S.D.M.A.S.S.
dc.contributor.authorJayaweera, N.
dc.contributor.authorJayasuriya, C.K.
dc.date.accessioned2021-12-29T04:47:34Z
dc.date.available2021-12-29T04:47:34Z
dc.date.issued2016
dc.description.abstractTitanium dioxide (Ti02) is the most widely used white pigment in the paint industry. TiO, is a photocatalyst under ultraviolet (UV) light. When it absorbs UV radiation, a UV photon which overcomes the energy gap between the valence and conduction bands of TiO, creates an electron-hole pair. The hole then reacts with water to produce hydroxyl radicals followed by a series of other reactions that produce more and more hydroxyl radicals which react with the organic matter to form water and carbon dioxide leading to the destruction of the polymeric binder of the paint film. This effect could be reduced by mixing the pigment with an inert oxide such as silica. The current research focuses on reducing photocatalytic effect of TiO2 and thereby increasing the durability of the paint. A series of emulsion paint samples were prepared according to an exterior paint formulation by varying the ratio Ti02:Si02. Formation of photocatalytic oxides were determined by measuring the absorbance using Orange II solution. Samples were exposed to UV radiation by applying them on small watch glasses as thin layers. The solution absorbance values on the samples were measured before and after exposure to UV radiation and recording absorbance at 60 min, 120 min and 240 min. The best sample with the lowest photocatalytic effect was used to determine paint properties. The lowest photocatalytic effect was observed for the sample containing 20% SiO2 and 80% of TiO2 and the paint properties were determined for that sample. Most of the properties are comparable with those of the industrial paint. However, viscosity and opacity are significantly reduced. It could be due to the undesired particle size of silica incorporated. Further investigations must be carried out to determine the optimum particle sizes which give the lowest photocatalytic effect with enhanced paint properties. Keywords: Photocatalytic Effect, Paint, Titania, Pigmenten_US
dc.identifier.isbn9789550481095
dc.identifier.urihttp://www.erepo.lib.uwu.ac.lk/bitstream/handle/123456789/8133/184-2016-Readucing%20Photocatalytic%20Degradation%20of%20exterior%20Paint%20Prepared%20with%20TiO2%20.pdf?sequence=1&isAllowed=y
dc.language.isoenen_US
dc.publisherUva Wellassa University of Sri Lankaen_US
dc.subjectMaterials Sciencesen_US
dc.subjectEngineeringen_US
dc.subjectTechnologyen_US
dc.subjectChemistryen_US
dc.subjectChemical Engineeringen_US
dc.titleReducing Photocatalytic Degradation of Exterior Paint Prepared with TiO2en_US
dc.title.alternativeResearch Symposium 2016en_US
dc.typeOtheren_US
Files
Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
184-2016-Readucing Photocatalytic Degradation of exterior Paint Prepared with TiO2 .pdf
Size:
45.6 KB
Format:
Adobe Portable Document Format
Description:
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
Research Symposium-2016