Surface Modification of Cellulose Micro Fibrils Extracted from Banana Pseudo-Stem Using Bis-[3-(triethoxysilyl) propyl] tetrasulfide
Loading...
Files
Date
2019-02
Journal Title
Journal ISSN
Volume Title
Publisher
Uva Wellassa University of Sri Lanka
Abstract
Cellulose as the most abundant biomolecule on the earth, it is on investigations to be used in several applications as a remedy for the exploitation of non-renewable resources and mismanagement of agro-industrial wastes. Banana (Musa sapientum) fibre is a promising source of cellulose which can be derived after harvesting while the majority of the pseudostems are used as a low-cost feedstock for the preparation of compost. However, the cellulose itself is not compatible with most of the materials especially, with non-polar matrices. Therefore, the extracted cellulose has to be surface modified. In this study, micro-fibrillated cellulose was prepared following an alkali treatment coupled with highpressure defibrillation and acid treatments on fibre extracted from pseudo-stem. The resulted micro-fibrillated cellulose was characterized using Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and cellulose structure was confirmed. XRD studies showed 69% crystallinity of micro-fibrillated cellulose. The particle size shows a bimodal distribution where approximately 21% of the sample has an average size of 110 nm and the rest is in averaged 795 nm. The prepared micro-fibrillated cellulose was surface modified using Bis-[3-(triethoxysilyl) propyl] tetrasulfide (TESPT) following rigorous solvent extractions with ethanol and acetone through cellulose membrane. With the surface modification, the percentage crystallinity has increased up to 77.8%. Moreover, the surface modification was confirmed by the results of FTIR spectroscopy showing the stretching vibration of Si-O-C bond at 1031 cm-1 indicating that the surface modification was successful.
Description
Keywords
Bioprocess Technology, Biotechnology, Bio Chemicals Engineering